Chemistry - Impregnating Materials

Depending on your individual requirements we offer different search and selection functions to help you find the appropriate material. The listed products are an extract from our actual product portfolio. More products are available on request.

Do you need further information about our impregnating materials? Please get in touch with us. We are looking forward to your email to impregnation.elantas.europe@remove-this.altana.remove-this-also.com.

 REQUEST TECHNICAL PRODUCT DATASHEET

 

Solvent based impregnating varnishes are typically resin based materials dissolved in non-reactive, organic solvents. With high tank stability, versatility, excellent film forming ability, good technical performance and a proven track record they remain highly relevant as impregnating materials.

Typical ELANTAS solvent based varnishes:

ProductViscosityTemperature IndexTypical Cure ScheduleDescription
Elmotherm®
F 93 A+B
10 - 20 s
ISO Cup 6 mm
23°C
18024 h / 23°C or
2 h / 100°C
Two component, solvented, finishing varnish, room temperature curing, very good film forming, excellent resistance to chemicals, available as colourless or red oxide. For dip, brush or spray application.
Elmotherm® FS19037 - 43 s
ISO Cup 6 mm
23°C
15524 h / 23°C or
2 h / 100°C
Single component, alkyd resin based, solvented finishing varnish, very good film forming, good resistance to moisture and chemicals, available colourless or red oxide. For dip, brush or spray application.
Elmotherm® 009-0008100 - 125 s
B4 Cup
21°C
1801 h / 23°C or
30 min / 80°C
Single component, UL recognised, alkyd resin based, solvented finishing varnish, fast air drying, available in a range of colours, colourless, golden, red oxide, black, grey and white. For dip, brush or spray application.
Elmotherm®
VA 160
25 35 s
Ford 4 Cup
25°C
15524 h / 25°C or
2 h / 80°C
Single component, UL recognised, alkyd resin based, solvented finishing varnish, fast air drying, available colourless or red oxide. For dip, brush or spray application.
Elmotherm®
UF 92 (N)
42 – 52 s
ISO Cup 6mm
23°C
1806 h / 130°C or
4 h / 120°C +
4 h / 150°C
Solvented varnish, UL recognised, without aromatic and halogenic components, elastic, resistant to lowest temperatures, for generators and drives in mining and shipbuilding. For dip and hot dip application.
Elmotherm® 073-1010135 – 165 s
B4 Cup
21°C
2006 h / 130°C or
2 h / 180°C
Solvented varnish, high build, excellent stability. Tough and resilient with excellent chemical resistance. Used by OEM's and repairers for electric motor stators and transformers. For dip and hot dip application.
Elmotherm®
VF 970
60 - 90 s
ISO Cup 6mm
25°C
2006 h / 130°C or
3 h / 150°C
Solvented varnish, high bond strength, excellent moisture, chemical and Freon resistance. Designed for impregnation of rotating electrical equipment. For dip and hot dip application.

 

Water based impregnating varnishes are typically modified resin bases, dissolved in water, often with a co-solvent. Emulsion technology is also used for this type of product. 

With a low environmental impact these materials are often a good, economical solution when replacing existing solvent based varnish technology.

Typical ELANTAS water based varnishes:

ProductViscosityTemperature IndexTypical Cure ScheduleDescription
Aquanel®
VF111
30 - 60 s
ISO Cup 6mm
25°C
1803h / 130°CWater-based varnish, UL recognised, low temperature curing, solvent free, for the general impregnation of electrical windings. For dip and hot dip application.
Aquanel® 014-3997/4035 - 45 s
B2 Cup
21°C
1803 h / 160°CSingle component, solventless emulsion, zero VOC, high bond strength, high chemical and moisture resistance, for the impregnation of stators, rotors and small transformers. For dip, hot dip and dip-roll application.
Aquanel®
H 2001
300 – 500 mPa.s
25°C
1803 h / 23°CSingle component, UL recognised, water based, epoxy modified varnish, low VOC. Good bond strength, moisture and chemical resistance. Suitable for motors, coils and transformers. Red pigmented version also available, Aquanel H2002. For dip and brush application.

 

These products are unsaturated polyester resin bases dissolved in a reactive monomer such as styrene or vinyl toluene. Emissions are reduced in comparison to solvent based varnishes, but are present to a significant level. 

These are typically low viscosity and highly reactive materials making them ideal for high productivity processes. With an ability to modify these resins, a range of final properties can also be achieved for any kind of impregnation processing plant.

Typical ELANTAS unsaturated polyester resins:

ProductViscosityTemperature IndexTypical Cure ScheduleDescription
Dobeckan®
FT 1052/…EK
100 – 110 s
ISO Cup 4 mm
23°C
1801 h / 150°CSingle component, UL recognised, polyester-imide resin, contains styrene, little secondary drainage, high filling ability, for processing of motors, generators and transformers. For dip and dip-roll application.
Dobeckan®
FT 2015/…EK
90 – 120 s
ISO Cup 4 mm
23°C
2001 h / 150°CSingle component, UL recognised, polyester-imide resin, contains vinyl toluene, little secondary drainage, high filling ability, excellent thermomechanical strength. For processing of motors, generators and transformers. For dip, dip-roll, VI and VPI application.
Dobeckan®
FT 1040/120
115 – 135 mPa.s
23°C
18030 min / 130°C or
15 min / 140°C
Two component, UL recognised, unsaturated polyester-imide resin, contains styrene, tough-hard material, for household machines and magnet wheels. For trickle application.
Dobeckan®
FT 1080/…
115 – 135 or
450 – 550 mPa.s
23°C
20030 min / 130°C or
15 min / 140°C
Two component, UL recognised, unsaturated polyester-imide resin, contains styrene, high bond strength, for processing of armatures and rotors. For trickle application.
Dobeckan®
FT 2001/…
115 – 135 or
470 – 520 mPa.s
23°C
18045 min / 130°C or
15 min / 150°C
Two component, UL recognised, unsaturated polyester-imide resin, contains styrene, excellent bond strength, for high speed power tools, starter motors and dynamos. For trickle application.
Dobeckan® FT2006-350 UV340 – 380 mPa.s
23°C
20030 mins / 150°C +
10 mins / 150°C UV
Single component, UL recognised, unsaturated polyester-imide resin, contains styrene, high elasticity and excellent thermal durability. For hot dip UV application of stators.

 

Low VOC unsaturated polyester resins are unsaturated polyester resin bases dissolved in reactive diluents that are non-volatile. These products provide a significant reduction in emissions compared to varnishes and monomer containing polyester resins, with excellent tank stability and viscosities that require little or no adjustment for existing impregnation processes. 

A high filling content in the windings is possible resulting in a high technical performance.

Typical ELANTAS low VOC unsaturated polyester resins:

ProductViscosityTemperature IndexTypical Cure ScheduleDescription
ELAN-protect®
UP 142
900 – 1500 mPa.s
23°C
1801 h / 150°C or
30 mins / 160°C
Single component, UL recognised, unsaturated polyester-imide resin, low viscosity, VOC free, high bond strength, quick surface drying, stable, for stators and rotors. For dip, hot dip, trickle and dip-roll application.
ELAN-protect®
UP 240
140 – 160 mPa.s
23°C
1801 h / 140°C or
30 min / 160°C
Two component, unsaturated polyester resin, contains acrylate, high reactivity, for small to medium size automotive alternators. For trickle and dip-roll application.
ELAN-protect®
UP 343
4500 – 5500 mPa.s
23°C
2002 h / 150°CSingle component, UL recognised, polyester-imide resin, crack-free curing in thick layers, excellent penetration capacity, high elasticity, for stators and transformers. For hot dip application.
Dobeckan®
825034
150 – 200 s
Ford 4 Cup
25°C
1802 h / 150°CSingle component, UL recognised, polyester resin, low viscosity, low emission, flexible and resilient, suitable for stators, transformers and general purpose use. For dip application.
Dobeckan® ST NV 075-4475850 – 1150 mPa.s
23°C
1802 – 3 h / 130°CSingle component, acrylated unsaturated polyester-imide resin, high thermal stability, for processing of traction armatures and field coils. For VPI application. 

Monomer free resins are specially synthesised unsaturated polyester resins that contain no monomers, solvents or reactive diluents. 

They provide a significant reduction in emissions compared to varnishes and monomer containing polyester resins, with excellent tank stability. With a relatively high viscosity, some adjustment to existing equipment and processing may be required.  

A high filling content in the windings is possible resulting in a high technical performance.

Typical ELANTAS monomer free unsaturated polyester resins:

ProductViscosityTemperature IndexTypical Cure ScheduleDescription
Dobeckan®
MF 8001 NV
6500 – 7500 mPa.s
23°C
1802 h / 150°CSingle component, UL recognised, unsaturated polyester resin, monomer and VOC free, medium viscosity, environmentally compatible. For hot dip, trickle and dip-roll application.
Dobeckan®
MF 8005
850 – 1150 mPa.s
23°C
118030 min / 150°C or
15 min / 160°C
Single component, UL recognised, unsaturated polyester resin, monomer and VOC free, low viscosity, environmentally compatible, high reactivity, stable, for small and medium size motors. For dip, trickle and dip-roll application.
Dobeckan®
MF 8044
6500 - 7500 mPa.s
23°C
18040 min / 150°C or
20 min / 160°C
Single component, UL recognised, unsaturated polyester-imide resin, stable, monomer and VOC free, environmentally compatible, high bond strength and excellent thermal durability. For hot dip, trickle, dip-roll. UV version also available.
Dobeckan®
MF 8001 UV2
8000 – 1000 mPa.s
23°C
18045 mins / 150°C +
15 mins / 150°C UV
Single component, UL recognised, unsaturated polyester-imide resin, stable, monomer and VOC free, environmentally compatible, good mechanical properties and excellent thermal durability. For hot dip UV application of stators.
Dobeckan®
MF 8004 UV
10000 – 12000 mPa.s
23°C
18045 mins / 150°C +
15 mins / 150°C UV
Single component, UL recognised, unsaturated polyester-imide resin, stable, monomer and VOC free, environmentally compatible, high bond strength and excellent thermal durability. For hot dip application. UV version also available. 

These products are unsaturated polyester resins pigmented white or black for the impregnation of lighting ballasts used in fluorescent lamps.  

Good penetration, filling content and strengthening of the windings results in significant noise reduction.

Typical ELANTAS pigmented unsaturated polyester resins:

ProductViscosityTemperature IndexTypical Cure ScheduleDescription
Dobeckan®
F 2504 E
55 - 65 s
ISO Cup 6 mm
23°C
180140°C / 1 hTwo component, unsaturated polyester resin, contains styrene, brilliant white, high covering power, designed for ballasts and transformers. For VI application.
Dobeckan®
F 2506 E
50 - 70 s
ISO Cup 6 mm
23°C
180140°C / 1 hTwo component, unsaturated polyester resin, contains styrene, brilliant white, low secondary drainage, designed for ballasts and transformers. For VI application.
Dobeckan®
FT 2402/150
130 - 170 s
ISO Cup 6 mm
23°C
180140°C / 1 hTwo component, UL recognised, unsaturated polyester resin, contains styrene, matt black, designed for ballasts and transformers. For VI application. 

These are formulated materials, using epoxy resin bases, diluents, catalysts and additives. Products based on this chemistry for impregnating materials are typically low or VOC free meaning emissions are significantly lower in comparison to varnishes and monomer containing products.

Epoxy resins are characterised by excellent tank stability, excellent chemical and moisture resistance with an overall high technical performance.

Typical ELANTAS epoxy resins:

ProductViscosityTemperature IndexTypical Cure ScheduleDescription
ELAN-protect®
EP 101#
400 – 2500 mPa.s
25°C
1803 h / 165°CSingle component, UL recognised, epoxy resin, low viscosity, excellent moisture and chemical resistance. Suitable for low voltage electric motor stators. For dip, hot dip, dip-roll and trickle application.
Epoxylite®
H 1009 #
1000 – 3500 mPa.s
25°C
1806 h / 130°C or
3 h / 165°C
Single component, epoxy resin, mechanically tough and resilient, excellent chemical and moisture resistance. Suitable for low voltage electric motors, coils and transformers. For dip, hot dip, VI and VPI application.
ELAN-protect®
EP 420
650 – 800 mPa.s
25°C
1806 – 12 h / 165°CSingle component, UL recognised, epoxy based resin, low VOC, low viscosity, for processing of low, medium and high voltage machines. For VPI application.
ELAN-protect®
EP 411
3300 - 5700 mPa.s
25°C
22012 h / 165°CSingle component, modified epoxy resin, high thermal stability, excellent chemical and moisture resistance, for processing of traction armatures and field coils. For VPI application.
Epoxylite®
578 EB #
3000 – 5000 mPa.s
25°C
1808 – 12 h / 165°CSingle component, thixotropic epoxy resin, zero VOC, for general purpose applications. For VPI application.
Epoxylite®
478
1700 – 2600 mPa.s
25°C
1806 h / 150°CSingle component, UL recognised, modified epoxy resin, resilient, high chemical and moisture resistance. Suitable for transformers. For VI and VPI application.
Epoxylite®
EIP 4526
190 – 210 mPa.s
25°C
1806 h / 165°CSingle component, epoxy resin, low stress, for processing of wound magnetic cores. For dip, hot dip, VI and VPI application. 
ELAN-protect® EP 2011000 – 2000 mPa.s
25°C
18045 min / 130°C or
20 min / 150°C
Single component, rapid curing, modified epoxy resin, with high thermal stability, excellent chemical and moisture resistance, designed for trickle / dip roll processing of rotating electrical machines.